钢材知识
耐热钢板(GB/T4238—1992)

(1)尺寸规格热轧钢板的尺寸规格和允许偏差应符合GB/T709《热轧钢板和钢带》的规定;冷轧钢板的尺寸规格应符合GB/T708《冷轧钢板和钢带》的规定。钢种按组织特征分为奥氏体型、铁素体型、马氏体型和沉淀硬化型四类。
(2)牌号和化学成分见表5-57~表5-60。表5-57奥氏体型耐热钢板的牌号和化学成分序号牌号化学成分质量分数)(%)CSiM1lPSNiCrM0V其他≤12Cr23-Nil3O.201.002.00O.035O.03012.00~15.0022.oo~24.0022Cr25-Ni20O.251.502.00O.035O.03019.00~22.0024.00~26.0031Crl6-Ni35O.151.502.000.035O.03033.00~37.0014.00~17.004OCrl5-Ni25Ti-2M0AlVBO.081.oo2.00O.035O.03024.00~27.0013.00~16.001.00~1.500.10~O.50Ti:1.90~2.35Al≥O.35B:0.00l~0.0105lCrl8-Ni9Si30.152.00~3.002.00O.0350.0308.00~lO.0017.00~19.0060Crl8Ni90.071.oo2.00O.035O.0308.00~11.0017.00~19.007OCr23-Ni130.081.002.00O.0350.03012.00~15.0022.00~24.0080Cr25-Ni200.081.002.00O.035O.03019.00~22.0024.00~26.009OCrl7Ni-12M020.081.002.00O.0350.03010.00~14.0016.00~18.002.00~3.0010OCrl9Ni-13M030.081.002.00O.035O.03011.00~15.0018.00~20.003.00~4.0011lCrl8-Ni9Ti0.121.002.00O.035O.0308.00~11.0017.00~19.00Ti≥5(wc一 0.02)~0.8012OCrl8Ni-10TiO.081.002.00O.0350.0309.00~12.0017.00~19.00Ti≥5×wc130Crl8-NillNbO.081.002.00O.035O.0309.00~13.0017.oo~19.ooNb≥10×wC14OCrl8-Ni13Si40.083.00~5.002.00O.0350.03011.50~15.0015.00~20.0015lCr20Ni-14S.20.201.50~2.501.50O.035O.03012.00~15.0019.00~22.0016lCr25Ni-20Si20.201.50~2.501.500.0350.03018.00~21.0024.00~27.00表5-58铁素体型耐热钢的牌号和化学成分序号牌 号化学成分(质量分数)(%)CSiMnPSNCrALTi≤171Crl9A130.101.501.000.0350.03017.oo~21.002.00~4.0018OCrll TiO.081.001.00O.0350.03010.50~11.756×Wc—O.75192Cr25NO.201.001.00O.035O.030O.2523.00~27.oo200Crl3Al0.081.001.00O.035O.03011.50~14.50O.10~0.302l00Crl20.031.001.000.035O.03011.00~13.0022lCrl70.12O.751.00O.035O.03016.00~18.00表5-59马氏体型耐热钢的牌号和化学成分序号牌号化学成分(质量分数)(%)CSiMnPSNiCr其 他≤23lCrl2O.150.501.00O.035O.030可≤O.6011.50~13.00Cu≤O.3024lCrl30.151.001.00O.0350.030可≤O.6011.50~13.50Cu≤0.30表5-60沉淀硬化型耐热钢的牌号和化学成分序号牌号化学成分(质量分数)(%)CSiMnPSMCrAlCu≤≤251Crl7Ni7A10.091.001.000.0350.0306.50~7.7516.00~18.000.75~1.500.50(3)交货状态钢板经热轧或冷轧后参照“力学和工艺性能”中的规定进行热处理,并进行酸洗或类似的处理,然后进行适当的矫直,经需方同意也可以省去酸洗等处理。(4)力学和工艺性能见表5—61~表5—64。表5-6l奥氏体型耐热钢的力学性能序号牌 号热处理温度/℃固溶(时效)拉力试验硬度试验óO.2óbδ5(%)HBSHRBHVMPa≥≤12Cr23Ni131030~1150,快冷2055604020l952lO22Cr25Ni201030~1180,快冷206590352019521031Crl6Ni351030~1180,快冷20556035201952104OCrl5Ni25Ti2-M0ALVB885~915或965~995,快冷(700~760×16h,空冷或缓冷)--5907259002515192≥24891≥10l202≥26l5lCrl8Ni9Si3lOlO~1150,快冷20552040207952186OCrl8M9lOlO~1150,快冷20552040187902007OCr23Ni131030~1150,快冷205520401879020080Cr25Ni201030~1180,快冷205520401879020090Crl7Ni12Mo2lOl0~1150,快冷2055204018790200lOOCrl9Nil3M031010~1150,快冷205520401879020011lCrl8Ni9Ti920~1150快冷205520401879020012OCrl8Ni11Ti920~1150,快冷205520401879020013OCrl8Ni11NB980~1150,快冷205520401879020014OCRl8Ni13Si4lOl0~1150,快冷2055204020795218151Cr20Ni14Si21080~1130,快冷59040161Cr25Ni20Si21080~1130,快冷54035表5-62铁索体型耐热钢的力学和工艺性能序号牌号热处理温度/℃(退火)拉力试验硬度试验弯曲试验óO.2óbδ5E(%)HBSHRBHVd一弯芯直径,a一钢板厚度MPa弯曲角度钢板厚度,mm≥≤<8≥8171Crl9A13780~950,快冷或缓冷2454401521095220180CrllTi780~50,快冷或缓冷1753652216280175180°d=ad=2a192Cr25N780~880,快冷2755lO2020195210135°d=ad=2a20OCrl3 A1780~830,快冷或缓冷1754102018388200180°d=ad=2a21OCrl2700~820,快冷或缓冷1953652218388200180°d=2a22lCrl7780~850,快冷或缓冷2054502218388200180°d=2a表5-63马氏体型耐热钢的力学和工艺性能序号牌号热处理温度/℃(退火)拉力试验硬度试验弯曲试验180°d一弯芯直径a一钢板厚度ó0.2óbδ5(%)HBSHRBHVMPa≥≤231Crl2750左右快冷或2054402020093210d=2a241Crl3800~900缓冷2054402020093210d=2a表5-64沉淀硬化型耐热钢的力学性能序号牌号热处理温度/℃拉力试验硬度试验ó0.2óbδ5(%)厚度/mmHBSHRCHRBHVMPa≤3>325OCrl7Ni7Al1000~1100固溶≤380≤1030≥20≥20≤190≤92≤200560时效≥960≥1140≥3≥5≥35≥3455lO时效≥1030≥1225不规定≥4≥40≥392(5)用途广泛用于石油、化工设备、锅炉、汽轮机、工业炉构件以及在高温下工作的其他构件。

 
友情链接
首页 | 公司简介 | 产品中心 | 现货资源 | 新闻中心 | 公司案例 | 钢材知识 | 营销网络 | 人才招聘 | 联系我们
上海钢顿实业有限公司 版权所有
地址:上海市宝山区宝林路516号418 网址:www.steeldun.com 电话:021-56116935 传真:021-56116925